Leading Manufacturer for Frp Pultruded Profiles - Hardener 2251 – Huabin
Leading Manufacturer for Frp Pultruded Profiles - Hardener 2251 – Huabin Detail:
Product Profile
Hardener 2251 is designed for epoxy resin and it is for heating operation under low temperature.
Technical indicator
|
Technical index |
Data |
|
Viscosity (25℃) |
50-100 |
|
Proportion (25℃) |
0.95 |
|
Amine value (mgKOH/g) |
300 |
|
Active hydrogen equivalent |
87 |
|
Gelation time (25℃/100g)minutes |
75 |
|
Film hardening time (25℃) hours |
6 |
|
Complete hardening time (70/25℃) hours |
18 |
Advantage
■ Low viscosity
■ High glossy
■ Long operation time
■ High mechanical strength
Mechanical property
| Mechanical property | Curing process | |
| Tensile strength | 60.5Mpa | 8hours fully cured at 50-60℃ |
| Bending strength | 96.6Mpa | 5hours fully cured at 70-80℃ |
| Bending failure load | 272N | |
| Tensile failure load | 2702N | |
Product Application
Epoxy floor artesian plane coating/casting material
FRP water softening tank production(winding technology)
Product detail pictures:
Related Product Guide:
Gaining client pleasure is our company's aim without end. We are going to make excellent efforts to create new and top-quality goods, meet your special requirements and provide you with pre-sale, on-sale and after-sale companies for Leading Manufacturer for Frp Pultruded Profiles - Hardener 2251 – Huabin, The product will supply to all over the world, such as: Rotterdam, Australia, Rome, If you need to have any of our merchandise, or have other items to be produced, make sure you send us your inquiries, samples or in depth drawings. Meanwhile, aiming to develop into an international enterprise group, we look forward to receiving offers for joint ventures and other cooperative projects.
By Vanessa from Colombia - 2018.11.11 19:52
The factory workers have a good team spirit, so we received high quality products fast, in addition, the price is also appropriate, this is a very good and reliable Chinese manufacturers.
By Phoenix from Sevilla - 2018.12.28 15:18