Leading Manufacturer for Frp Pultruded Profiles - Hardener 2251 – Huabin Detail:
Product Profile
Hardener 2251 is designed for epoxy resin and it is for heating operation under low temperature.
Technical indicator
|
Technical index |
Data |
|
Viscosity (25℃) |
50-100 |
|
Proportion (25℃) |
0.95 |
|
Amine value (mgKOH/g) |
300 |
|
Active hydrogen equivalent |
87 |
|
Gelation time (25℃/100g)minutes |
75 |
|
Film hardening time (25℃) hours |
6 |
|
Complete hardening time (70/25℃) hours |
18 |
Advantage
■ Low viscosity
■ High glossy
■ Long operation time
■ High mechanical strength
Mechanical property
| Mechanical property | Curing process | |
| Tensile strength | 60.5Mpa | 8hours fully cured at 50-60℃ |
| Bending strength | 96.6Mpa | 5hours fully cured at 70-80℃ |
| Bending failure load | 272N | |
| Tensile failure load | 2702N | |
Product Application
Epoxy floor artesian plane coating/casting material
FRP water softening tank production(winding technology)
Product detail pictures:
Related Product Guide:
With a sound business credit, excellent after-sales service and modern manufacturing facilities, we have earned an excellent reputation among our customers across the world for Leading Manufacturer for Frp Pultruded Profiles - Hardener 2251 – Huabin, The product will supply to all over the world, such as: USA, Cyprus, kazan, We attained ISO9001 which provides solid foundation for our further development. Persisting in "High quality, Prompt Delivery, Competitive Price", we have established long-term cooperation with clients from both overseas and domestically and get new and old clients' high comments. It is our great honor to meet your demands. We are sincerely expecting your attention.
By Julie from South Africa - 2017.06.29 18:55
The customer service reprersentative explained very detailed, service attitude is very good, reply is very timely and comprehensive, a happy communication! We hope to have a opportunity to cooperate.
By Chloe from Grenada - 2018.09.23 18:44