Low MOQ for Epoxy Resin For Frp Water Tank - Hardener 2251 – Huabin
Low MOQ for Epoxy Resin For Frp Water Tank - Hardener 2251 – Huabin Detail:
Product Profile
Hardener 2251 is designed for epoxy resin and it is for heating operation under low temperature.
Technical indicator
|
Technical index |
Data |
|
Viscosity (25℃) |
50-100 |
|
Proportion (25℃) |
0.95 |
|
Amine value (mgKOH/g) |
300 |
|
Active hydrogen equivalent |
87 |
|
Gelation time (25℃/100g)minutes |
75 |
|
Film hardening time (25℃) hours |
6 |
|
Complete hardening time (70/25℃) hours |
18 |
Advantage
■ Low viscosity
■ High glossy
■ Long operation time
■ High mechanical strength
Mechanical property
| Mechanical property | Curing process | |
| Tensile strength | 60.5Mpa | 8hours fully cured at 50-60℃ |
| Bending strength | 96.6Mpa | 5hours fully cured at 70-80℃ |
| Bending failure load | 272N | |
| Tensile failure load | 2702N | |
Product Application
Epoxy floor artesian plane coating/casting material
FRP water softening tank production(winding technology)
Product detail pictures:
Related Product Guide:
We not only will try our greatest to offer superb companies to just about every buyer, but also are ready to receive any suggestion offered by our shoppers for Low MOQ for Epoxy Resin For Frp Water Tank - Hardener 2251 – Huabin, The product will supply to all over the world, such as: Morocco, kazan, Nigeria, Our solutions have national accreditation standards for experienced, premium quality items, affordable value, was welcomed by people around the globe. Our goods will continue to increase in the order and look forward to cooperation with you, Really should any of those products be of interest to you, please letus know. We are going to be pleased to give you a quotation up on receipt of one's detailed specifications.
By Jodie from Surabaya - 2017.10.23 10:29
Timely delivery, strict implementation of the contract provisions of the goods, encountered special circumstances, but also actively cooperate, a trustworthy company!
By Nicole from Austria - 2017.10.25 15:53